关键词
热喷涂，铝，修复
引用文件
下列文件中的条款通过本规范的引用而成为本规范的条款。凡是注日期的引用文件，其随后所有的修改单（不包括勘误的内容）或修订版均不适用于本规范，然而，鼓励根据本规范达成协议的各方研究是否可使用这些文件的最新版本。凡是不注日期的引用文件，其最新版本适用于本规范。
序号
文件编号
文件名称
每个表面上取至少5个点进行测试，其值必须符合以下要求：平均Ra值低于12.5μm。
2.3
所有工件均应进行厚度检测。
按ISO 2178进行检测。在零件表面，凡能被直径为20 mm的球接触到的区域，厚度均应在60～150μm范围内；凡直径为20 mm的球不能接触到的区域，其厚度不作要求。
2.4
每生产批至少检查一件工件或样件。
4Procedure of ProcessAuthentication
The factory to be appraised should complete all the following tests upon condition that the parts are produced in batches.
GB/T 4956
4
ISO 2409
Paint and Varnish-Cross-Cut Test
GB/T 9286
5
DKBA0.450.0012
Requirements for Chemical Conversion Coating on Aluminum and Its Alloys
Term & Definition
GB/T 9286
5
DKBA0.450.0012
铝及铝合金化学转化膜质量要求
术语和定义
术语
定义
生产批
指同一天在相同条件下处理的、材料和形状相似的零件的总和。
1
1.1
热喷涂铝工艺只适用于对钢板基材或铝材所进行的局部修复处理、或者表面局部导电化处理。
生产者的工艺设备、工艺流程、质量保证措施应在其主要的工艺文件中加以说明。
Term & Definition
Explanation
Batch
The sum of the parts with the similar materials and shape that are processed in the same conditionson the same day
1Requirements for ProcessAuthentication
生产者的工艺质量必须满足第1.2至1.6节的要求。
1.2
1）热喷涂铝处理必须在工件喷涂有机涂层后进行。
2）热喷涂铝涂层进行化学转化的后处理，可以采用刷涂、喷涂或浸涂等各种方式。
1.3
被鉴定的工厂必须完成以下全部试验工作，这些试验必须在零件批生产所用的条件下完成：
1）试样加工（注1）
2）表面处理（注2）
表目录
图目录
热喷涂铝涂层质量要求
Qualityrequirements forThermal Spraying coating ofAluminum
范围
本规范规定了热喷涂铝涂层的工艺和质量要求。
本规范适用于对钢板材料或铝材表面进行局部修复而进行的处理。
简介
本规范对热喷涂铝的适用场合、基材对象、加工工艺流程及其后处理限制以及铝涂层的质量要求作出了明确规定。其中质量要求包括外观、膜厚、表面粗糙度、耐蚀性、结合力等。
2.1
所所有工件都应进行外观检查。
铝涂层应呈哑白色，结晶均匀、致密、连续。无起皮、鼓泡、大熔滴、裂纹、掉块和严重水纹印等缺陷。
与粉末涂层的交界边缘应整齐，无疏松颗粒，不露底材金属；而且铝层应覆盖一些粉末层形成过渡，过渡区宽度为1～3mm左右（如下图所示）。
图2过渡区示意图
2.2
每生产批工件抽检至少一件。
1.5.5
在三件试样上进行耐蚀性试验。
经化学转化处理后的铝涂层应符合DKBA0.450.0012的要求，即按IEC 60068-2-11进行盐雾试验应通过100H。
1.6
经过华为技术有限公司鉴定的工艺，在未得到华为技术有限公司的同意之前，不能改变任何可影响性能质量的工艺参数，否则将重新进行鉴定.。
2
3）试样检查及测试（按1.4节）
4）提供试验报告（注3）及试片给华为技术有限公司以便复验。
注：1、鉴定用试样也可由华为技术有限公司完成并提供给被鉴定工厂。
2、所有试样必须同时进行处理。
3、试验报告的发出者必须是华为技术有限公司认可的试验室或单位。
1.4
1.4.1
材料：冷轧钢板
尺寸：80×125×1～4 (mm)
3Requirements for Process
The process of thermal aluminum spraying cannot be implemented unless an organic coating is sprayed to thepart.
The thermal sprayed coating of aluminum must undergo the chemical conversion after-treatment by means of brushing, spraying, or dip-coating.
Keywords
Thermal spraying, aluminum, and repair
Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of the specifications. For dated references, subsequent amendments, excluding corrections, to, or revisions of, any of these publications do not apply. However, parties to agreements based on this specification are encouraged to investigate the possibility of applying the most recent editions of the normative documents. For undated references, the latest edition of the normative document referred to applies.
2General Principle
The process of thermal aluminum spraying is only applicable to local repair of the steel plate matrix or aluminum material, or local conductive treatment on the surface.
Brief Introduction
The technical specifications expressly stipulate the applicable scenarios, matrix materials, process flow, and after-treatment restrictions of thermal aluminum spraying, as well as the quality requirements for the aluminum coating. The quality requirements cover its appearance, film thickness, surface roughness, corrosion resistance, and binding strength.
No.
Document No.
Document Title
Equivalent
1
IEC 60068-2-11
Basic environmental testing procedures. Part 2 : Tests. Test Ka: Salt mist
GB 2423.17
ASTM B117
2
ISO 1463
3
制定本规范参考的文献，但没有直接引用里面的内容
序号
文献编号或出处
文献名称
1
GB 9795
热喷涂铝及铝合金涂层
2
实用新型专利说明书CN 2676567Y
导电屏蔽机柜机箱的构件
Table of Contents
List ofTables
List of Figures
热喷涂铝涂层质量要求
Quality requirements forThermal Spraying coating ofAluminum
按ISO 2409的试验方法，在试样上划出2mm见方的小格，然后用标准胶带（3M公司的Scotch 250#）拉扯，应无任何涂层脱落现象。
2.5
在试样上进行耐蚀性试验；每生产批至少检测三件。
经化学转化处理后的铝涂层应符合DKBA0.450.0012的要求，即应通过100H的盐雾试验（按IEC 60068-2-11进行）。
1.5
1.5.1
所有试样均应进行外观检查。
铝涂层应结晶均匀、致密、连续。经化学转化后外观符合转化膜相关要求。
不允许：起皮、鼓泡、大熔滴、裂纹、掉块和严重水纹印。
1.5.2
所有试样均应进行粗糙度检测。
用粗糙度测量仪器在每个试样上取至少5个点进行测试，其值必须符合以下要求：平均Ra低于12.5μm。