目录第一部分设计任务书 ....................................1.1 设计题目 ······························································1.2 设计依据 ······························································1.3 设计内容及要求 ·····················································第二部分设计说明书.....................................2.1 前言 ····································································2.2 物料衡算 ······························································2.3 系统工艺流程的确定 ···············································2.4 设备选型 ······························································2.5 结论 ····································································第二部分设计说明书2.1前言浮法工艺优点多例如建设快，质量好，产量高，成本低，品种多等。
所以为进一步提高产品质量和产量，节约成本，我们将使用浮法工艺来生产玻璃！玻璃组成的设计原则：1)设计的玻璃组成能够满足给定的性能要求2)设计的玻璃组成易于形成玻璃，析晶倾向小3)设计的玻璃组成能够适合一定的熔制，成型，退火，加工等生产工艺条件4)设计的玻璃组成应当价格低廉，原料易于获得SiO2：硅砂，硅石粉降低玻璃热膨胀系数，提高热稳定性、化学稳定性、软化温度、硬性机械强度AL2O3：硅砂，白云石降低玻璃的结晶倾向，提高玻璃的化学稳定性和热稳定性、机械强度、硬度和折射率Fe2O3：硅砂，石灰石属于杂质，少量可以引起玻璃着色CaO：石灰石，白云石能增加的化学稳定性，在高温时能够降低玻璃的粘度，有利于玻璃的澄清和融化，在温度降低时，玻璃的粘度增加，成型后必须立刻进行退火，否则易炸裂MgO：白云石可以改善玻璃的成型性能，降低结晶倾向和结晶速度，增加玻璃的高温粘度，提高玻璃的化学稳定性和机械强度Na2O：纯碱，芒硝可以降低玻璃的粘度，使玻璃易于融化，有利于降低溶质温度，节约能源的作用，是最好的助熔剂。
碎玻璃可以节约原料，加速玻璃熔制过程，节约能耗，提高融化率，有利于澄清和均化，改善成型性能，而且保管简便2.2物料的衡算物料衡算的目的：计算各种原料的需要量以及从原料进厂至成品出厂各工序所需处理的物料量，作为工厂原料需要量，运输量，工艺设备选型计算的依据根据玻璃组成和所用的化学组成来进行配料计算。
在计算中。
应该认为在加热的过程中全部分解逸出，而分解后的氧化物则全部转入玻璃组成中去。
随着对制品质量要求不断的提高，必须考虑会影响玻璃组成的各种因素。
例如，耐火材料的侵蚀，原料的飞料损失以及玻璃的组成等。
因而在配料计算时，应对某些组成作适当的增件和修正，以保证设计组成尽如期望而实现。
1 工艺参数（1）芒硝含率芒硝含率指由芒硝引入的Na2O 与芒硝和纯碱引入的Na2O总质量之比，即芒硝含率=芒硝中引入Na2O量/芒硝中引入的Na2O量+纯碱中引入的Na2O量芒硝含率随原料供应和熔化情况而异，一般应该在3%---6%之间（2）碎玻璃掺入量碎玻璃掺入率指配合料中碎玻璃用量与配合料总量之比，即碎玻璃掺入量=碎玻璃量/生料量+碎玻璃量它随着熔化条件与碎玻璃的贮存量而增减，正常情况下一般应为15%---25%表1 原料成分表表2原料配方玻璃获得率83% 芒硝含率5%碎玻璃掺入量23% 计算基础100Kg玻璃液计算精度0.011.纯碱和芒硝的用量芒硝（A）：42.79%A／13.88=5%纯碱（B）：B= （13.88-0.4279A）/0.5791解得A=1.619537275B=22.73700572.硅砂与硅石粉的用量，分别设为M和N0.9160M+0.9935N=72.400.0421M+0.0034N=1.00解得M=19.30514996N=55.074466673.白云石和石灰石的用量，分别设为a和b0.31a+0.54b=8.2-0.100386779-0.0826117=8.0170015210.212a+0.0094b=4.20-0.032818764-0.055074466=4.11210677解得a=19.22788163b=3.8080707724.对硅砂和硅石粉用量的校正，分别设为x和y0.9160x+0.9935y=72.40-0.769115269-0.09900984=71.531874890.0421x+0.0034y=1.00-0.076911528-0.015232283=0.907856189解得x=17.01669347Y=56.3106654硅砂中含Na2O的量为0.546235865.对芒硝和纯碱的用量校正芒硝(x): 42.79x/(13.86-0.54623586)=5%纯碱(y):y=(13.86-0.54623586-0.4279x)/0.5791解得x=1.555709762Y=21.84091855表5 生产100Kg玻璃液物料用量碎玻璃的掺入量为A，原料总量为BA+83%B=100A/B=23/77解得碎玻璃掺入量为26.46玻璃获得率为100/119.77=83.49%表3 生产400t浮法玻璃需要的原料2.3 系统工艺流程的确定硅砂，硅石粉直接购买外面的合格粉料，不用粉碎，进入料仓白云石购买块状，回来经过破碎和粉磨，筛分后进入料仓纯碱购买的有粉料和块状的，块状的经过颚破，筛分后进入料仓芒硝购买的块状的回来经过笼形碾破碎后筛分进入料仓碎玻璃有本厂所得，经破碎后，洗涤，风干进入料仓工艺流程图混合料→窑头料仓→熔窑→锡糟→退火窑→切割→检验装箱----堆垛→包装工艺流程图见2#图纸2.4设备的选型进行设备选型的原则：1)选出的设备应满足既定的生产能力要求并适应工艺操作的特点2)设备的型式，数量应适应玻璃厂的生产规模及当地的自然地理条件3)设备要便于操作，工作可靠，并最大限度地节省投资及经营费用，并注意的安全，密封，便于收尘4)尽量采用已成批生产的技术上先进成熟的设备粉碎机械：颚式破碎机，对辊破碎机，笼形碾，反击式破碎机颚式破碎机优点构造简单，管理和修理方便，工作安全可靠，适用范围广对辊破碎机优点结构简单，机体不高，紧凑轻便，造价低廉，工作可靠，调整粉碎度方便，能粉碎粘湿物料笼形碾优点构造简单轻便，对物料湿度变化反应较小反击式破碎机优点结构简单，制造维修方便，工作时无显著不平衡振动，无需笨重的基础，效率高，生产能力大，电耗低，磨损少，产品粒度均匀筛分机械：六角筛，单层振动筛称量设备：电子配料称混合机械：强制混合机起重运输机械：皮带输送机，斗式提升机加料机械：电磁振动给料机硅砂和精砂的筛分熔制玻璃用硅砂的颗粒直径应在0.15-0.8mm之间，其中0.25-0.5mm的颗粒应不少于50％，0.1mm以下的不超过5％。