药芯焊丝牌号对照表序号符合相当标准GB AWS JIS 结构钢用药芯焊丝1GB/T 10045-2001 E500T-1A5.20 E70T-1Z3313 YFW-C50DR 2GB/T 10045-2001 E501T-1A5.20 E71T-1 Z3313 YFW-C50DR 3GB/T 10045-2001 E500T-5A5.20 E70T-5Z3313 YFW-C503B 4------------A5.29E81T1-Ni1Z3313 YFW-C603R 5GB/T 10045-2001 E500T-1A5.20 E70T-1Z3313 YFW-C50DR 6---------------------Z3313 YFL-C504R 7---------------------Z3320 YFA-50W8GB/T 17493-1998 E550T1-W A5.29 E80T1-W Z3320 YFA-58W 耐热钢用药芯焊丝9GB/T 17493-1998 E551T1-A1 A5.29E81T1-A1Z3318 YFM-C10GB/T 17493-1998 E551T1-B1A5.29E81T1-B1Z3318 YFCM-C11GB/T 17493-1998 E551T1-B2A5.29E81T1-B2Z3318 YF1CM-C12--------------------------------13GB/T 17493-1998 E601T1-B3 A5.29E91T1-B3Z3318 YF2CM-C气保焊不锈钢药芯焊丝14GB/T 17853-1999 E308T1-1A5.22E308T-1Z3323YF308C15GB/T 17853-1999 E308LT1-1A5.22E308LT-1Z3323YF308LC16GB/T 17853-1999 E309T0-1A5.22 E309T-1Z3323 YF309C17GB/T 17853-1999 E309LT0-1A5.22E309LT-1Z3323 YF309LC18GB/T 17493-1999 E309MoT0-1 ----------Z3323 YF309MoC 19GB/T 17853-1999 E316T0-1A5.22 E316T-1 Z3323 YF316C20GB/T 17853-1999 E316LT0-1A5.22E316LT-1Z3323 YF316LC21GB/T 17853-1999 E347T1-1A5.22 E347T-1Z3323 YF347C 22GB/T 17853-1999 E410T0-1A5.22 E410T-1Z3323 YF410C 23GB/T 17853-1999 E430T0-1A5.22 E430T-1Z3323 YF430C 不锈钢TIG焊用药芯焊丝24(相当)GB/T 17853-1999 E308T1-5A5.22 E308T-2Z3323 YF308C25GB/T 17853-1999 R308LT1-5A5.22E308LT-2Z3323 YF308LC26(相当)GB/T 17853-1999 E309T1-5A5.22 E309T-2Z3323 YF309C27GB/T 17853-1999 R309LT1-5A5.22E309LT-2Z3323 YF309LC28----------------------Z3323 YF309MoC 29(相当)GB/T 17853-1999 E316T1-5A5.22 E316T-2Z3323 YF316C30GB/T 17853-1999 R316LT1-5A5.22E316LT-2Z3323 YF316LC31GB/T 17853-1999 R347T1-5A5.22 E347T-2Z3323 YF347C MAG焊用耐磨堆焊药芯焊丝32--------------------------------33--------------------------------34--------------------------------35--------------------------------36--------------------------------37--------------------------------埋弧焊用耐磨堆焊药芯焊丝38--------------------------------39--------------------------------40--------------------------------41--------------------------------42--------------------------------序中国钢廉日本神户韩国现代号1------------DW-100F------------2GL-YJ502(Q)DW-100SF-713GL-YJ507(Q)------------------------4GL-YJ602(Q)DW-60------------5------------MX-100SF-70MX6GL-YJ502Ni(Q)------------------------7GL-YJ502CrNiCu(Q)DW-50W SF-70W8GL-YJ602CrNiCu(Q)DW-588SF-80W 耐热钢用药芯焊丝9------------------------------------10------------------------------------11GL-YR302(Q)DW-1CMA------------12------------------------------------13GL-YR402(Q)DW-2CMA------------气保焊不锈钢药芯焊丝14GL-YA102(Q)DW-308------------SW-308L 15GL-YA002(Q)DW-308LCored16GL-YA302(Q)DW-309------------SW-309L 17GL-YA062(Q)DW-309LCored18------------------------------------19GL-YA202(Q)DW-316------------SW-316L 20GL-YA022(Q)DW-316LCoredSW-347 21GL-YA132(Q)DW-347Cored23------------DW-430Nb------------不锈钢TIG焊用药芯焊丝24------------------------------------25------------------------------------26------------------------------------27------------------------------------28------------------------------------29------------------------------------30------------------------------------31------------------------------------------------ MAG焊用耐磨堆焊药芯焊丝32------------DWH-250------------33GL-YD350(Q)DWH-350------------34GL-YD450(Q)DWH-450------------35------------DWH-600------------36------------DWH-800------------37------------------------------------埋弧焊用耐磨堆焊药芯焊丝气保护药芯焊丝使用说明:碳钢药芯焊丝，执行GB/T10045-2001标准；低合金钢药芯焊丝，执行GB/T17493-1998标准；不锈钢药芯焊丝，执行GB/T17853-1999标准药芯焊丝是上世纪70年代逐步发展起来的，由于它效率高、节能、工艺性能好、质量高、综合成本低（只有手工焊条的1/2，埋弧焊丝的1/3，CO2实芯焊丝的90%）、飞溅少，已成为21世纪新一代焊材。
值得提出是化学成分可根据需要进行调整，甚至可以用低碳钢带通过药芯合金成分制成不锈钢药芯焊丝，这是其它焊材难以达到的，药芯焊丝的成本、熔敷速度及飞溅比较可见下图：位置种类熔敷速度焊接电流电流范围平焊Ⅰ95 280 120-300 Ⅱ90 280 100-350Ⅲ70 110 250-330 立向上Ⅰ72 220 120-260 Ⅱ40 150 100-300Ⅲ38 190 130-300 立向下Ⅰ98 280 260-300 Ⅱ60 320 200-300 横焊Ⅰ98 280 120-300 Ⅱ95 280 100-300Ⅲ38 250 170-250 仰焊Ⅰ93 230 120-260 Ⅱ40 150 100-200Ⅲ36 180 130-200注：Ⅰ-药芯焊丝，Ф1.2mm；Ⅱ-实芯焊丝，Ф1.2mm；Ⅲ-焊条，Ф5.0mm金桥焊材药芯焊丝分为气保护药芯焊丝和自保护药芯焊丝两大类，其具有以下特点：（一）气保护药芯焊丝1、在一定的焊接参数下，可进行全位置焊接。
2、熔敷效率高，调整合金成分方便。
3、药芯能改变熔滴过渡的特点，从而可减少飞溅和改善焊缝成型。
4、由于是CO2气体和熔渣联合保护，因而可有效地防止气孔。
5、飞溅很少。
（二）自保护药芯焊丝1、在一定焊接参数下，可进行全位置焊接。
2、熔敷效率较高，调整合金成分方便。
3、穿透力强，单面焊双面成型。
4、野外施工不需保护气体，有一定的抗风能力。
5、力学性能优良，特别是低温冲击韧性很好。
CHW-50C2产品描述:CHW-50C2符合：GB ER50-2相当：AWS ER70S-2说明：CHW-50C2是镀铜低合金钢焊丝，采用CO2或80%Ar＋20% CO2作为保护气体进行施焊。
具有优良的焊接工艺性能，电弧稳定、飞溅少、焊丝含较高的脱氧物质，特别适于焊接区域有一定的油、油漆、锈、水的焊接。
但焊缝低温韧性不高。
用途：用于450及500Mpa级强度的碳钢及低合金钢（如高层建筑、野外作业等）的单道或多道、对接或角接的焊接。