PRO30496 introduction -New oligomer for glass ink and coating application
Kenji – 2011.Nov.12nd
PRO30496 introduction
PRO30496 is designed for glass screen ink that required
2
Transparent 6140mpa·s 14.75 3H 5B(Gt 0) >2hr
PRO30496 introduction
It can be applied for various glass printingscontainers ,bottles, Home appliances, bath and kitchen appliances, etc
3
Built-in formulation Evaluation
Glass ink formulation for evaluaຫໍສະໝຸດ ionIngredients
PRO30496 Silane A-174(硅烷偶联剂) Pigment(颜料) Talc (滑石粉) Fumed silica R-974(气相二氧化硅) BYK 9076(Dispersant分散剂)) TSA 750S(Defoamer硅烷消泡剂) BYK307(levelling agent流平剂) Irgacure 907 Irgacure 369 ITX EDAB
for good boiling water resistance, which also has good properties balance. It’s suitable for both screen Inks and Coatings
PRO30496 Appearance Viscosity@25℃ APHA(Gardner) Pencil Hardness Adhesion to glass Boiling water resistance
6
Thank you for your attention!
7
％
75.00 1.55 8.00 6.14 1.55 0.52 0.52 0.50 2.07 2.07 1.04 1.04
Application Process(油墨应用方法 油墨应用方法) 油墨应用方法 Drying 60oc x 20min 或80oc x 10min
油墨印在玻璃上以后,需要烘干后才能进行紫外曝光固化.这 是因为PRO30496中含有少量溶剂,曝光时间温度可参考上 面参数,也可根据具体情况来调整
Mixing until temperature become around 40dC Triple Roll Mill (Particle size max. < 10.0um) Total
100.00
No gloss reduction No Whitening spots after boiling for 2hours
Ink properties(油墨最终性能 油墨最终性能) 油墨最终性能 Printability Adhesion to Glass Pencil Hardness Boiling water resistance* Water soaking @RT Good 5B(Gt 0) 2H >2hr >1 month
Our result was gained by applied PRO30496 directly with spray after diluted to suitable viscosity
5
Built-in formulation Evaluation
Ink with PRO30496 after 2 hours boiling water
4
Built-in Ink Evaluation
Spray coating evaluation
leveling Adhesion to Glass Pencil Hardness Diluted to suitable viscosity Boiling water resistance Water soaking @RT Good 5B(Gt 0) 2H >2hr >1 month