The perfect match –
BASF raw materials for two component polyurethane coatings
Dr. Rainer Erhardt, BASF SE
Team Leader Technical Marketing Automotive & Industrial Coatings,
Resins and Additives Europe
New 2K PU Brochure
Content
⏹100 % Coatings based on bio-based polyols (application: pipeline coating) ⏹Super high-solid flexible coating with excellent adhesion on PVC
(application: truck tarpaulin coating)
⏹Water-borne coatings showing fast drying performance,
early block resistance and high hardness
What do natural oil based polyols (Sovermol®) offer to polyurethane coatings/adhesives manufacturers?
⏹Bio-based Polyols (polyfunctional alcohols) based on
renewable raw materials like rapseed oil, Castor oil,
soybeen oil etc. treated with technologies like
epoxidation followed by ring-opening,
transesterification, ethoxylation or propoxylation
⏹Unique properties:
⏹Improved hydrophobicity;
low sensitivity towards moisture
⏹Low viscosity
⏹High chemical stability
⏹Broad adhesion spectrum
⏹Very low shrinkage
⏹High pigment loading with good self levelling
properties …EASY to APPLY“
⏹Solvent free – ZERO VOC
Construction kit approach to customer needs
Solvent free 2-pack PUR Pipeline Coating
Guide Formulation 805-1092/55 (aromatic polyisocyanate cured)
Equipment: Dissolver or vacuum dissolver. Ratio of Ø dissolver blade to Ø container approx. 6 : 10
Airless sprayable at 50 °C
Solvent free 2-pack PUR Pipeline Coating
Guide Formulation 805-1092/55
Salt spray test – Coating (170 µm) without primer on non-sandblasted steel.
Solvent free 2-pack PUR Pipeline Coating
Guide Formulation 805-1092/55
Salt spray test – Coating (170 µm) without primer on non-sandblasted steel.
Content
⏹100 % Coatings based on bio-based polyols (application: pipeline coating) ⏹Super high-solid flexible coating with excellent adhesion on PVC
(application: truck tarpaulin coating)
⏹Water-borne coatings showing fast drying performance,
early block resistance and high hardness
Super high-solid flexible coating formulation (Joncryl® / Sovermol®) (DF13-28 Jan)
Suppliers (1) BASF SE
Super high-solid flexible coating formulation (Joncryl® / Sovermol®) (DF13-28 Jan)
Key characteristics:
⏹Extremely flexible
⏹Rubberlike surface
⏹High chemical resistance (> 200 MEK double rubs)
⏹Good adhesion on various plastics (example: PVC)
⏹Fast chemical drying
⏹High gloss
⏹Very hydrophobic
⏹Very low VOC (283 g/l at 20s DIN 4 flow cup time)
Content
⏹100 % Coatings based on bio-based polyols (application: pipeline coating) ⏹Super high-solid flexible coating with excellent adhesion on PVC
(application: truck tarpaulin coating)
⏹Water-borne coatings showing fast drying performance,
early block resistance and high hardness
Joncryl® OH 8311 (primary dispersion) (DF_06/09/2011)
Suppliers (1) BASF SE
(2) Air products
(3) Elementis Specialties
Joncryl® OH 8311 (DF_06/09/2011)
Hardness Development
Pendulum hardness @ 23 °C
50 µm dry film thickness
Substrate: glass
Joncryl® OH 8311 (DF_06/09/2011)
Coating Properties
(Binder: secondary dispersion) (DF_06/09/2011)
Suppliers (1) Supplier A
(2) BASF SE
(3) Air Products www.airproducts.de
(4) OMG Borchers www.borchers.de
(Binder: secondary dispersion) (DF_06/09/2011)
Hardness Development
Calculation osc in sec Array
Pendulum hardness @ 23 °C
50 µm dry film thickness
Substrate: glass
(Binder: secondary dispersion) (DF_06/09/2011) Array Basonat® HW 3180 B:
Forced drying (60 °C or higher)
necessary for chemical crosslinking
Thanks to all contributors
Georg Bourscheidt
Oliver Kowald
Daniel Flojhar
Angelika Enckler
Nicolas Wiemer
Sabine Schmierl。