改性沥青的研究进展黄 彬,马丽萍,许文娟(昆明理工大学环境科学与工程学院,昆明650093)摘要 为了得到性能更优良的改性沥青,越来越多的材料被用作改性沥青改性剂,同时新的评价标准和方法及其他领域的新化学分析方法也被用来更完整准确地评价改性沥青的性能。
总结了国内外改性沥青的研究现状及进展,从改性机理、性能影响因素及评价方法等方面来介绍各种改性沥青的概况,并概述了改性沥青的发展方向。
关键词 改性沥青 改性剂 机理 发展Rsearch Development of Modif ied AsphaltHUAN G Bin ,MA Liping ,XU Wenjuan(Faculty of Environmental Science and Engineering ,Kunming University of Science and Technology ,Kunming 650093)Abstract More materials ,as modifier ,are used to improve the properties of modified asphalt.Besides ,the new evaluation standards and methods ,new chemical analysis methods are used to evaluate the properties more com 2pletely and accurately.The situation and development of modified asphalt research at home and abroad are summa 2rized.From the aspcts of modification mechanism ,influencing factors and evaluation methods ,various modified as 2phalts are introduced ,and the development trend of modified asphalt technology is illustrated in the paper.K ey w ords modified asphalt ,modifier ,mechanism ,development 黄彬:女,1986年生,硕士研究生,主要研究方向为固体废物资源化 E 2mail :binbin_huang @ 马丽萍:女,1966年生,教授,主要研究方向为工业废气污染控制、固废综合开发利用 E 2mail :lipingma22@0 前言普通道路沥青由于自身的组成和结构决定了其感温性能差,弹性和抗老化性能差,高温易流淌,低温易脆裂。
而且在过去的10年中,车轴负荷增加、车流量增加、气候条件恶劣,难以满足高级公路的使用要求,必须对其改性以改善使用性能。
在沥青或沥青混合料中加入天然或合成的有机或无机材料,熔融或分散在沥青中与沥青发生反应或裹覆在沥青集料表面,可以改善或提高沥青路面性能。
1 改性沥青的分类在沥青的改性材料中,高分子聚合物是应用最广泛、研究最集中的一种。
其他改性材料还有两大类:矿物质填料和添加剂。
矿物质填料,如硅藻土、石灰、水泥、炭黑、硫磺、木质素、石棉和炭棉等,对沥青进行物理改性,可提高沥青抗磨耗性、内聚力和耐候性。
添加剂,包括抗氧化剂和抗剥落剂,如有机酸皂、胺型或酚型抗氧化剂或阴、阳离子型或非离子型表面活性剂,可提高沥青粘附性、耐老化或抗氧化能力。
聚合物改性沥青(PMA 、PMB ),按照改性剂的不同一般可分为3类:①热塑性橡胶类,即热塑性弹性体,主要是嵌段共聚物,如SBS 、SIS 、SE/BS ,是目前世界上最为普遍使用的道路沥青改性剂,并以SBS 最多;②橡胶类,如NR 、SBR 、CR 、BR 、IR 、EP 2DM 、IIR 、SIR 及SR 等,以胶乳形式使用,其中SBR 应用最为广泛;③树脂类,如EVA 、PE 、PVC 、PP 及PS 。
2 各种改性沥青及其发展现状通过SCI 和EI 分别检索近15年来改性沥青在交通、建筑、材料、能源及环境等学科方面研究的文献情况,检索结果如图1、图2及表1、表2所示。
根据表1、表2数据和图1、图2情况可以看出,近几年国内外对改性沥青的研究越来越多,尤其以SBS 和胶粉最为突出,出现了多种新型改性剂。
下面将分别介绍各种改性沥青及其发展现状。
图1 SCI 检索统计表Fig.1 SCI search results2.1 矿物质材料改性沥青矿物质材料作改性剂的研究较少,主要为硅藻土、纳米碳酸钙、矿渣粉、白炭黑等,可与基质沥青形成均匀、稳定的共混体系以改善沥青性能[1]。
表1 SCI 检索统计表Table 1 SCIsarch rsult s序号主题词文献篇数全部2009-20052004-20001999-19951995年以前1TS =Modified asphalt649340186107162TS =(Modified asphalt and rubber )131********TS =(Modified asphalt and SBS )11360391314TS =(Modified asphalt and EVA )24166205TS =(Modified asphalt and SBR )1482406TS =(Modified asphalt and EBA )321007TS =(Modified asp halt and PE )1064008TS =(Modified asphalt and PP )330009TS =(Modified asphalt and PVC )3120010TS =(Modified asphalt and waste )4828155表2 EI 检索统计表Table 2 EI search result s序号主题词文献篇数全部2009-20052004-20001999-19951TS =Modified asphalt11155872972312TS =(Modified asphalt and rubber )23911054753TS =(Modified asphalt and SBS )198********TS =(Modified asphalt and EVA )2011545TS =(Modified asphalt and SBR )2515286TS =(Modified asphalt and EBA )42117TS =(Modified asphaltand PE )139408TS =(Modified asphalt and PP )55009TS =(Modified asphalt and waste )88272437图2 EI 检索统计表Fig.2 EI search results鲍燕妮等[2]从分离机理、试验验证分析方面对硅藻土改性沥青相容性进行了研究,为硅藻土改性沥青的实际应用提供了一定理论依据,并在我国云南大保高速铺设了试验路,结果显示实际路用性能较好。
张志清等[3]认为硅藻土具有特殊的微观结构,能吸收沥青的油分,有助于改善沥青的路用性能。
硅藻土不仅起填料作用,更主要的是改性作用,当硅藻土含量为14%时能显著提高混合料的高温稳定性并改善低温抗裂性。
马峰等[4]运用沥青的四组分分析、红外光谱和差示扫描量热分析等实验手段发现纳米碳酸钙掺加到基质沥青中能形成均匀、稳定的共混体系,改善和提高了沥青性能。
张兴友等[5,6]采用美国SHRP 计划动态剪切试验方法对硅藻土、白炭黑(精细化工新产品,主要成分为二氧化硅)等进行研究,发现其能够很好地改善高温性能、低温性能、水稳定性和抗疲劳性能。
2.2 添加剂改性沥青搭配合适的阴、阳离子混合表面活性剂增效作用显著,但是目前的开发、应用研究还很不够。
这一技术应用的潜力很大,各个领域都应积极开发,只要掌握其搭配的规律,提高应用技术,定会产生显著的经济效益。
樊芷芸等[7]在阳离子表面活性剂(季铵盐类)和阴离子表面活性剂(烷基苯磺酸盐)物质的量比为5∶1的条件下,制备了O/W 乳化沥青,并对其在水利防渗工程中的应用进行了研究。
结果表明,利用阴、阳离子混合表面活性剂制备的沥青乳液稳定性提高,表面活性剂的用量也大幅度减少,从而使成本降低。
他们还把这种阴/阳离子表面活性剂混合体系乳化沥青用于制备乳化沥青混凝土,其渗透系数满足了水利工程防渗要求,并具有热稳定性好、力学性质受温度影响小等优点,可用于一般水利防渗工程,特别适用于暴露在大气中受温度影响较大的部位,给施工带来很大的方便。
2.3 聚合物改性沥青2.3.1 苯乙烯丁二烯嵌段共聚物SBSSBS是由1,32丁二烯和苯乙烯通过阴离子聚合而得到的线型或星型嵌段共聚物。
在SBS的嵌段共聚物中,由于聚苯乙烯与聚丁二烯在常温时的不相容性,共聚物中分子链之间的聚苯乙烯内聚能密度较大,故其两端首先分别与另外的聚苯乙烯聚集在一起,形成许多约束成分的物理交联区域,但又因其嵌段是柔性的聚丁二烯嵌段,就形成了网状结构。
SBS改性的优越性突出表现在使软化点大幅度提高的同时,又使低温延度明显增加,感温性得到很大改善,而且弹性恢复率特别大。
目前,大部分改性沥青研究都是围绕SBS进行的,SBS 在实际研究中改性效果相当好。
国内做的比较好的是兰亭高科,他们自主开发了SBS改性沥青、乳化SBS改性沥青技术及成套设备技术。
SBS改性沥青最大的问题是稳定性。
日本从改善相容性着手来保证改性沥青体系的稳定性:掺入大量芳香分以利于SBS与沥青之间形成界面吸附层,同时掺加大量树脂,用以弥补烃质油分导致产品软化点降低的不足,此方法成本很高、操作也很复杂。
美国曾用硫化的方式,让硫原子渗入SBS与沥青之间产生反应,此法很难掌握控制,往往会引起沥青的凝胶化而使沥青成为废品。
Guian Wend等[8]通过研究SBS改性沥青发现,加入10%的硫磺可以有效改善改性沥青的存储稳定性。
兰亭高科开发了WD 热贮存稳定剂,提高了热贮存稳定性,也提高了产品的路用性能[1,9]。
2.3.2 聚乙烯(PE)和乙烯2醋酸乙烯共聚物(EVA)常用于沥青改性的有低密度乙烯LDPE和线型低密度聚乙烯。
研究发现当PE在沥青中掺量超过5%时,由于其粘度较大,混合物在高速搅拌过程中会发生蠕变,PE较难分散。
随PE分子量的增大,在相同掺量下,粘度也会增大[10,11]。
PE改性沥青以奥地利RF集团的产品Novophalt为代表。